供应抗紫外线POM，107，507美国杜邦均聚甲醛DuPont

详情描述：

   POM      107      美国杜邦公司 物性数据①原料描述部分规格级别：注塑级外观颜色：---用途概述：---备注说明：特性：均聚甲醛，强度、刚度、热稳定性能好、硬度好。②原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位其它性能弯曲降服强度+73HASTM D-79014.3MPsi基本性能密度---ASTM D-7921.42---物理性能吸水量24hrs浸泡+73H(+23℃)ASTM D-5700.25%吸水量Equil.50%R.h.+73H(+23℃)ASTM D-5700.22%吸水量浸泡均衡点+73H(+23℃)ASTM D-5700.90%扩散因数+73H(+23℃)106HzASTM D-1500.005---机械性能洛氏硬度---ASTM D-785M94,R120---摩擦系数+73H(+23℃)静态ThrustWasherTest30.20---摩擦系数+73H(+23℃)动态ThrustWasherTest30.35---挠曲系数+122℃在25℃下620MPa弯曲降服强度+23℃ASTM D-79098.6MPa压缩应力+73H@1%Def.ASTM D-6955.2MPsi挠曲系数+70℃在25℃下1550MPa挠曲系数+212H在25℃下130MPsi挠曲系数+100℃25℃下895MPa挠曲系数+250H在25℃下90MPsi弹性系数+23℃ASTM D-6383100MPa剪力+73HASTM D-7329.5MPsi剪力+23℃ASTM D-73265.5MPa挠曲系数-68H在25℃下530MPsi挠曲系数-55℃在25℃下3650MPa挠曲系数+73H在25℃下380MPsi挠曲系数+23℃在25℃下2620MPa挠曲系数+158H在25℃下225MPsi断裂时之拉力伸张度-68H(-55℃)ASTM D-63838%断裂时之拉力伸张度+73H(+23℃)ASTM D-63875%断裂时之拉力伸张度+158H(+70℃)ASTM D-638230%断裂时之拉力伸张度+212H(+100℃)ASTM D-638>260%断裂时之拉力伸张度+250H(+122℃)ASTM D-638>260%伸张强度-68HASTM D-63814.7MPsi伸张强度-55℃ASTM D-638101MPa伸张强度+73HASTM D-63810.0MPsi伸张强度+23℃ASTM D-63868.9MPa伸张强度+158HASTM D-6386.9MPsi伸张强度+70℃ASTM D-6386.9MPa伸张强度+212HASTM D-6385.2MPsi伸张强度+250HASTM D-6383.8MPsi伸张强度+122℃ASTM D-63826.2MPa伸张强度+100℃ASTM D-63835.9MPa弹性系数+73HASTM D-638450MPsi压缩应力+23℃@1%Def.ASTM D-69535.9MPa压缩应力+73H@10%DefASTM D-69518.0MPsi压缩应力+23℃@10%Def.ASTM D-695124MPa负载下之变形2000psi@+122H(14Mpa@50℃)ASTM D-6210.5%弯曲疲劳忍耐限度+73HASTM D-6714.7MPsi弯曲疲劳忍耐限度+23℃ASTM D-67132.4MPaIZOD冲击强度-40HASTM D-2561.8ft.lb/inIZOD冲击强度40℃ASTM D-25696.1j/mIZOD冲击强度+73HASTM D-2562.3ft.lb/inIZOD冲击强度+23℃ASTM D-256123j/m拉力冲击抵抗力+73HD1822Long170ft.lb/in2拉力冲击抵抗力+23℃D1822Long350kj/m2无切口冲击程度+73HASTM D-256>100(no break)ft.lb/in无切口冲击程度+23℃ASTM D-256>5300(no break)j/m电气性能电阻系数+73H(+23℃)0.2%H2OASTM D-2571015ohm-cm绝缘系数+73H(+23℃)102to106HzASTM D-1503.7---绝缘强度Short Time,90 milsASTM D-149500V/mil绝缘强度Short Time,2.3mmASTM D-14919.7MV/m电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.热 性 能可燃烧性---UL-9494HB---热传导系数------2.6BTU-in/hr热传导系数------0.37W/mk线性热膨胀系数+140 to +220HASTM D-6967.610-5in/in.H线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃线性热膨胀系数+220 to +300HASTM D-6968.310-5in/in.H线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃熔点---ASTM D-2133347H熔点---ASTM D-2133175℃线性热膨胀系数-40 to +85HASTM D-6965.810-5in/in.H线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃线性热膨胀系数+85 to +140HASTM D-6966.810-5in/in.H线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃热变形温度264psiASTM D-648277H热变形温度1.8MPaASTM D-648136℃热变形温度66psiASTM D-648342H热变形温度0.5MPaASTM D-648172℃